对ＰＳＺ－Ｍｏ系梯度功能材料（ｆｕｎｃｔｉｏｎａｌｌｙｇｒａｄｉｅｎｔｍａｔｅｒｉａｌｓ简称ＦＧＭ）在制备过程中的热应力缓和性能进行了优化设计，用有限元方法解析了ＰＳＺ－Ｍｏ系两层叠层材料（即非梯度功能材料）在制备过程中的热应力分布情况。同时解析了ＰＳＺ－Ｍｏ系ＦＧＭ在制备过程中的热应力分布及缓和规律。揭示了ＰＳＺ－Ｍｏ系ＦＧＭ在制备过程中的热应力大小与组成分布形状指数Ｐ的关系，对所研究的体系通过热应力解析，得到制备中热应力缓和最佳时的Ｐ值，同时，对ＦＧＭ的制备工艺进行了研究，用粉末法分别制备出２４ｍｍ×５．６ｍｍ和３０ｍｍ×５ｍｍ完整的ＦＧＭ试样。 The thermal stress relaxation behavior of PSZ-Mo graded FGMs was optimized. The finite element method was used to analyze the thermal stability of PSZ-Mo graded FGMs (ie, non-gradient functional materials) The process of thermal stress distribution. At the same time, the thermal stress distribution and relaxation rules of PSZ-Mo FGM were analyzed. The relationship between the thermal stress and the shape index P of the PSZ-Mo FGM was revealed. The P value of the thermal stress in the system under study was obtained by the thermal stress analysis. At the same time, FGM preparation process was studied, the powder method were prepared 24mm × 5.6mm and 30mm × 5mm intact FGM sample.