The effects of various cooling paths on uniformity of through-thickness microstructure and mechanical properties of X80 pipeline steel of 22.0 mm in thickness were studied. The finite difference method was employed to calculate the temperature field during cooling. It was confirmed by the experimental result and temperature field calculation that the optimizing process was achieved by the ultra-fast cooling with medium cooling capacity(cooling rate of *23 K/s)followed by ultimate cooling capacity(cooling rate of *50 K/s). After optimization, the experimental steel displayed much uniform microstructure and the deviation of through-thickness hardness was controlled within 20 HV. In addition,the yield strength, tensile strength and elongation of the experimental steel were 621, 728 MPa and 21.5%, respectively,meeting the requirements of the API standard for X80 pipeline steels.
The effects of various cooling paths on uniformity of through-thickness microstructure and mechanical properties of X80 pipeline steel of 22.0 mm in thickness were studied. The finite difference method was employed to calculate the temperature field during cooling. It was confirmed by the experimental result and temperature field calculation that the optimizing process was achieved by the ultra-fast cooling with medium cooling capacity (cooling rate of * 23 K / s) followed by ultimate cooling capacity (cooling rate of * 50 K / s). steel exhibited much uniform microstructure and the deviation of through-thickness hardness was controlled within 20 HV. In addition, the yield strength, tensile strength and elongation of the experimental steel were 621, 728 MPa and 21.5% respectively, meeting the requirements of the API standard for X80 pipeline steels.