【摘 要】
：
通过对1.5mm厚的TRIP600 MPa钢板进行系列疲劳试验,对试验数据进行拟合处理,用扫描电镜观察疲劳断口形貌。结果表明,在加载频率为8 Hz、R=0的高周拉-拉疲劳试验条件下,TRIP60
论文部分内容阅读
通过对1.5mm厚的TRIP600 MPa钢板进行系列疲劳试验,对试验数据进行拟合处理,用扫描电镜观察疲劳断口形貌。结果表明,在加载频率为8 Hz、R=0的高周拉-拉疲劳试验条件下,TRIP600钢板的疲劳极限为460 MPa;S-N曲线拟合的经验公式为:lgN=51.1625-16.8574 lgσ;钢板的疲劳源多位于表面下的夹杂物处,裂纹的扩展区为韧性断裂,瞬断区为脆性断裂。
A series of fatigue tests were carried out on a 1.5 mm thick TRIP600 MPa steel. The experimental data were fitted and the morphology of the fatigue fracture was observed with a scanning electron microscope. The results show that the fatigue limit of TRIP600 steel plate is 460 MPa under high-tension-pull fatigue test with loading frequency of 8 Hz and R = 0. The empirical formula of SN curve fitting is: lgN = 51.1625-16.8574 lgσ; Most of the fatigue sources were located at the subsurface inclusions, the crack extension zone was ductile fracture, and the transient zone was brittle fracture.
其他文献
Phylogenetic methods have been widely used to detect the evolution of influenza viruses.However, previous phylogenetic studies of influenza viruses do not make
目的:探讨无锡市哮喘儿童和过敏性鼻炎儿童吸入性过敏原检测诊断情况,为合理选择诊断方法提供参考.方法:选择80例哮喘患儿与80例过敏性鼻炎患儿分别进行皮肤点刺试验(SPT)与
目前已知有8个基因位点与青光眼有关,其中2个有关原发性开角青光眼(primary open-angle glauco-ma,POAG)基因已被确定:MYOC/TIGR基因编码myocilin,主要与青少年型POAG有关;另
自行研制了双管及多管填砂模型,通过改变填砂管长度模拟了流线长度比为1.00、1.10、1.25和1.41的4组双管蒸汽驱实验以及1组四管并联的多管蒸汽驱实验,研究了蒸汽波及系数、采
目的:探讨非小细胞肺癌微血管密度(MVD)与256层螺旋CT扫描强化增强值之间的关系。方法:选择河北联合大学附属医院2010年7月到2011年7月间经胸心外科收治并于术前接受256层螺
目的: 分析、研究滇重楼的抑菌谱.方法:利用液体稀释法分别测定滇重楼两种方法提取物对11种细菌的抑菌作用.结果:滇重楼对金黄色葡萄球菌、伤寒沙门菌、普通变形杆菌、铜绿假
通过金相观察统计以及夹杂物电解与能谱分析,对不同批号72A盘条产品索氏体化率以及夹杂物类型与尺寸进行研究.结果表明,72A盘条中的夹杂物主要为尺寸小于20μm的氧化物夹杂,
维吾尔语作为一种典型的黏着语,通过丰富的功能词缀来表达各种语法和语气.该文探讨了“词干词性标注方法”与“词缀词性标注方法”在维吾尔语自然语言处理中的优缺点.在大规
采用固相法合成制备La2/3Sr1/3MnO3∶Agx(LSMO∶Agx,其中x为Ag掺杂量的摩尔比,x=0.00、0.10、0.20、0.30、0.40)多晶材料。通过X射线衍射和R-T对LSMO:Ag x材料的结构和性能进
分别对6063铝合金原样与硫酸直流阳极氧化法处理样品样进行铜加速盐雾腐蚀,考查时间对腐蚀样品形貌、元素分布及电化学腐蚀行为的影响,利用质量损失法对腐蚀动力学进行分析。