【摘 要】
:
The arc erosion under medium direct currents in the argon flow was tested on tungsten-copper (W-Cu) contacts which were processed by hot extrusion and heat treatment. The scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were u
【机 构】
:
School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang 471
【出 处】
:
武汉理工大学学报(材料科学版)(英文版)
论文部分内容阅读
The arc erosion under medium direct currents in the argon flow was tested on tungsten-copper (W-Cu) contacts which were processed by hot extrusion and heat treatment. The scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used to study the microstructure of the W-Cu powders and compacts. The contact resistance, arcing energy, and arcing time were continuously measured by JF04C contact materials test system. Changes in tungsten-copper contact surface were observed by SEM. The test results showed that the arcing time and arcing energy all increase with current and voltage, but the changes of average contact resistance are more complicated. For a short arcing time, the average contact resistance decreases with increasing current due to the vaporization of Cu. However, for a longer arcing time, it slightly increases due to the formation of high resistant films, compound copper tungsten. The formation of compound copper tungsten was confirmed by the increased Rc kept in the range from 1.1 to 1.6 mΩ. The compound copper tungsten is first exposed with a tungsten and copper-rich surface, and then totally exposed due to evaporation of copper from the surface. At last a stabilized surface is created and the crystals decrease from 8 μm to 2 μm caused by the arc erosion.
其他文献
A novel epoxy-imide resin based on diglycidyl ether of bisphenol-A and N-(4-hydroxyphenyl) terahydrophthalic anhydrideimide (HTAM) was synthesized. The structural characterization of the epoxy-imide resin was conducted by FT-IR spectra. 4,4\'-diaminodip
One interpenetrating network hydrogel based on sodium alginate (SA) and polyvinyl alcohol (PVA) was synthesized by combining the raw materials of PVA and SA with the double physical crosslinking methods of freezing thawing and Ca2+ crosslinking. The PVA-S
The pullout behavior of large-diameter collapsed double-walled carbon nanotubes (DWCNT) was studied by molecular dynamics simulations and compared with those in the circular cross-sectioned state. The pullout force-displacement curves of both are in good
Using a walnut shell as a carbon source and ZnCl2 as an activating agent, we resolved the temperature gradient problems of activated carbon in the microwave desorption process. An appropriate amount of silicon carbide was added to prepare the composite ac
We investigated synthesis and characterization of melamine-urea-formaldehyde (MUF) microcapsules containing n-alkane mixture as phase change core material for thermal energy storage and low-temperature protection.The phase change microcapsules (microPCMs)
NaCl aqueous solution (15wt%) was used as the quenching medium to prepare amorphous Lithium-Zinc ferrite hollow microspheres (LiZn FHMs) based on self-reactive quenching technology. Investigations by scanning electro microscope, X-ray diffraction, electro
The interaction mechanism and phase evolution of ammonium polyphosphate (APP) mixed with muscovite (APP/muscovite) were studied by TG, XRD and SEM, respectively, during heating. When the temperature is not higher than 300℃, muscovite has no effect on the
The objective of this paper was to develop a comprehensive evaluation method and index to evaluate the performance of sealants and fillers for cracks in asphalt concrete pavements using the method of principal component analysis.The performance experiment