The formation and aggravation of hydrogen damage in Fe-3 wt-% Si alloy during cathodiccharging Were studied by means of Lange transmission X-ray topography.Results showedthat hydrogen damage did not form in the specimens charged in 0.5 mol/L H<sub>2