【摘 要】
：
The effects of aging on mechanical properties,intergranular corrosion and exfoliation corrosion behaviors of a 2197 type A1-Li alloy were investigated,and the m
【机 构】
：
School of Materials Science and Engineering,Technology Center
论文部分内容阅读
The effects of aging on mechanical properties,intergranular corrosion and exfoliation corrosion behaviors of a 2197 type A1-Li alloy were investigated,and the mechanisms were studied through microstructure observation and electrochemical measurement of simulated bulk phase.The main strengthening precipitates of the alloy aged at175 ℃ and 160 ℃ are δ and T1.T1 precipitation in the alloy aged at 160 ℃ is delayed,which results in its slower age strengthening and over-aging behavior than the alloy aged at 175 ℃.Meanwhile,aging temperature of 160 ℃causes more uniform distribution and finer size of T1,resulting in its better strengthening effect.As aging time and aging temperature are increased,the size of T1 at grain boundaries and the width of PFZ along grain boundaries are increased,leading to an increase in the susceptibility to intergranular corrosion and exfoliation corrosion.It is suggested that better comprehensive properties can be obtained when the alloy is aged at 160 ℃.
其他文献
N, O-carboxymethyl chitosan ( CMCTS ), a kind of biodegradable organic substance, was added to calcium phosphate bone cement (CPC) to produce a composite more s
Hydroxyapatite ( HA )-reinforced high density polyethylene (HDPE) was developed as a bone replacement material. In order to enhance the interfacial bondiag betw
La2O3-doped CaO-MgO-Nb2O5-TiO2 system ceramics were prepared by solid-state ceramic technique. The microstructure and microwave dielectric properties of CaO-MgO
The bio- inspired strategy of triggered release of Ca2 +, Pi, F from prosomal compartments was used to induce rapid formation of FHA for potential dental use: C
The author applied extended BCF/BCFW rules with fermions to a set of simple electroweak processes in colliders. In such processes, there are two electroweak cha
The precipitation processes of γand θ phases in Ni75 Al6.5 V18.5 alloy were simulated at different temperatures and the precipitation sequence of two phases a
The addition of graphite powder in conventional asphalt mixture can produced asphalt concrete with excellent electrical performance. Percolation theory was empl
Fibrous hydroxyapatite ( HA ) was grown upwards from the crosslinked unsaturated polyphosphoester( UPPE ) which was used as an injectable bone tissue engineerin
Characteristic and dynamic viscosities of Hyaluronic acid ( HA ) derivative modified by polyethylene glycol (PEG) were tested with different reaction times (6 h
The black nickel formation process in leaching solution containing ammonia and chloride was investigated in terms of cyclic voltammetric and galvanostatic reduc