A low carbon steel with Cr addition of 0.46wt% combined with trace elements of Mn and Ti was studied.The apparent activation energy of deformation and the hot d
ZE10 magnesium alloy was subjected to equal-channel angular pressing(ECAP) up to 12 passes in a die with an angle of 120° between the two channels at 250-300°