Thermo-mechanical process and continuous cooling process were carried out on 20 CrNi2MoV steel. Three cooling rates were implemented to optimize the mechanical properties. The microstructure evolution, precipitation behavior, and strengthening mechanisms were systematically investigated, and the fracture mechanisms were analyzed via combination of impact fracture morphologies and deflection–load curves. The experimental results indicate that the transformed microstructure of experimental steel is all complex consisting of granular bainitic ferrite and bainitic ferrite with dispersed martensite/austenite(M/A) constituents in the matrix at cooling rates of 13, 21, and 29 °C/s. When the cooling rate increases, the grain of the steel is obviously refined. The sizes of the bainitic ferrite are 5.8, 4.7, and 3.1 lm under cooling rates of 13, 21, and 29 °C/s, respectively. The refinement of the bainitic ferrite plays a dominant role in strength increasing and also contributes to high crack propagation energy. However, the morphologies of M/A constituents obtained under different cooling rates contribute to different crack initiation energies and then affect the impact property.
Thermo-mechanical process and continuous cooling process were carried out on 20 CrNi2MoV steel. Three microscopic rates were implemented to optimize the mechanical properties. The microstructure evolution, precipitation behavior, and strengthening mechanisms were systematically investigated, and the fracture mechanisms were analyzed via combination of impact fracture morphologies and deflection-load curves. The experimental results that that the transformed microstructure of experimental steel is all complex consisting of granular bainitic ferrite and bainitic ferrite with dispersed martensite / austenite (M / A) constituents in the matrix at cooling rates of 13 , 21, and 29 ° C / s. When the cooling rate increases, the grain of the steel is obviously refined. The sizes of the bainitic ferrites are 5.8, 4.7, and 3.1 lm under cooling rates of 13, 21, and 29 ° C / s, respectively. The refinement of the bainitic ferrite plays a dominant role in strength increasing and also contributes to high crac However, the morphologies of M / A constituents obtained under different cooling rates contribute to different crack initiation energies and then affect the impact property.