It is well-known that the application of ultrasound during liquid to solid transitions for alloys can refine the solidification microstructure and thus improves the mechanical properties. However, most published work focuses on single phase dendritic growth, whereas little has been conducted on the multiphase alloys with complicated phase transformations during solidification. In this work, the solidification process of ternary Cu40Sn45Sb15 alloy was realized within intensive ultrasonic field with a resonant frequency of 20 k Hz and ultrasound power from 0 W to 1000 W. The ultrasound refines the size of the primary e(Cu3Sn) intermetallic compound by two orders of magnitudes. If the ultrasound power increases to 1000 W, g(Cu6Sn5) phase nucleates and grows directly from parent liquid phase without the occurrence of peri-eutectic reaction on the top of the alloy sample where the ultrasound intensity is sufficiently high. These microstructural variations lead to the enhancement of compressive strength and elasticity modulus of ternary Cu40Sn45Sb15 alloy.
It is well-known that the application of ultrasound during liquid to solid transitions for alloys can refine the solidification microstructure and thus improves the mechanical properties. However, most published work focuses on single phase dendritic growth, little little has been conducted on the multiphase alloys with complicated phase transformations during solidification. In this work, the solidification process of ternary Cu40Sn45Sb15 alloy was realized in intensive ultrasonic field with a resonant frequency of 20 k Hz and ultrasound power from 0 W to 1000 W. The ultrasound refines the size of the primary If the ultrasound power increases to 1000 W, g (Cu6Sn5) phase nucleates and grows directly from parent liquid phase without the occurrence of peri-eutectic reaction on the top of the alloy sample where the ultrasound intensity is sufficiently high. These microstructural variations lead to the enhancement of compress ive strength and elasticity modulus of ternary Cu40Sn45Sb15 alloy.