The structural evolution of ZA27 alloy modified by element Zr was studied during semi solid isothermal heat treatment, and its transformation mechanism was also discussed. The results indicate that the primary α phase changes from equiaxed grains to spherical grains gradually at semi solid temperature of 460 ℃. With increasing isothermal time, the eutectic between boundaries of α phase diffuses toward α phase, and the primary equiaxed grain arms merge and boundaries tend to disappear to form near particle grains. Further, the eutectic left on α boundaries melts to make the near particle grains separate, and form spherical structure at last. [
The structural evolution of ZA27 alloy modified by element Zr was studied during semi solid isothermal heat treatment, and its transformation mechanism was also discussed. The results indicate that the primary α phase changes from equiaxed grains to the spherical grains gradually at semi solid temperature of 460 ° C . With increasing isothermal time, the eutectic between boundaries of α phase diffuses toward α phase, and the primary equiaxed grain arms merge and boundaries tend to disappear to form near particle grains. Further, the eutectic left on α boundaries melts to make the near particles grains separate, and form spherical structure at last. [