Specifications of inclusions such as the type, morphology, number, composition, size, and place of inclusions in HK40 heat-resistant casting steel were studied by optical microscopy and scanning electron microscopy equipped with an energy-dispersive spectroscopy system. The effects of calcium silicide (CaSi) addition on these characteristics were evaluated at two pouring temperatures of 1420℃ and 1470℃. It was found that most of the appeared inclusions were in the type of chromium oxide. CaSi addition had a significant effect on the morphological modification, size and distribution of inclusions as well as changing the composition to oxide-sulfide compounds. Specifications of inclusions such as the type, morphology, number, composition, size, and place of inclusions in HK40 heat-resistant casting steel were studied by optical microscopy and scanning electron microscopy equipped with an energy-dispersive spectroscopy system. The effects of calcium silicide (CaSi) addition on these characteristics were evaluated at two pouring temperatures of 1420 ° C. and 1470 ° C. It was found that most of the appeared inclusions were in the type of chromium oxide. CaSi addition had a significant effect on the morphological modification, size and distribution of inclusions as well as changing the composition to oxide-sulfide compounds.