本文通过对试制的复合活化混凝土掺合料进行试验研究,结果表明:该掺合料最佳水胶比为0.42,取代水泥最佳比例为30%。其新拌混凝土缓凝时间较长,坍落度损失小,具有混凝土所要求的良好工作性能。所配制的混凝土早期强度增长低于纯水泥混凝土,但后期强度增长较快,其混凝土的抗收缩、抗渗等长期耐久性能均能得到有效的改善与提高。 In this paper, the trial production of composite activated concrete admixtures were studied. The results showed that the optimal water-cement ratio of this admixture was 0.42, and the optimal ratio of cement was 30%. Its fresh concrete retarded a long time, slump loss is small, with the required good performance of concrete. The early strength of the prepared concrete is lower than that of the pure cement concrete, but the strength increases rapidly in the later period. The long-term durability of concrete such as anti-shrinkage and impermeability can be effectively improved and improved.