我所与北京钢厂等单位协作研制成功热锻模新钢种——35Cr3Mo3W2V(以下简称HM1),成分符合我国资源,冶炼容易,锻造和机械加工综合性能好,制成模具使用寿命高,最近已组织鉴定,
论文部分内容阅读
我所与北京钢厂等单位协作研制成功热锻模新钢种——35Cr3Mo3W2V(以下简称HM1),成分符合我国资源,冶炼容易,锻造和机械加工综合性能好,制成模具使用寿命高,最近已组织鉴定,北京钢厂已投产。该钢已由北京钢厂、贵阳钢厂等冶炼近100吨,钢材合格率100%,成材率82%,经十几个厂点的试验,轴承环毛坯热锻模寿命由原来的3000件提
Our cooperation with Beijing Steel and other units successfully developed a new type of hot forging steel - 35Cr3Mo3W2V (hereinafter referred to as HM1), composition in line with China’s resources, easy smelting, forging and machining performance is good, made of high service life of the mold, the recent Has been identified, Beijing Steel has been put into operation. The steel has been smelting nearly 100 tons of steel from Beijing Steel, Guiyang Steel and other steel, steel pass rate of 100%, finished product rate of 82%, after more than a dozen factory tests, bearing ring blank hot forging die life from the original 3000
其他文献
我厂柱塞泵青铜座内球面加工,是生产上一项关键,原采用高速钢四刃球形铰刀分粗精两次铰削加工。由于零件精度、光洁度要求都比较高(见图1),着色检查接触面积要求达80％以上。
The Executive Committee of China 2009 World Stamp Exhibition held the Secretary-General’s Official Meeting in Luoyang on Mar. 10, 2008. It was presided
The Ex
图1所示冷挤压加工用整形模,材料T10,热处理要求内孔硬度HRC56～58。我们在RJX-60炉中加热,每炉装3件,795±10℃,保温3.5小时,采用图2的装置用10%NaCI水溶液冲水淬火,
Cold e
氧化和脱碳是合金元素与气体介质相互反应和物理扩散过程中所产生的一种铸造缺陷。防止这种缺陷的产生有二种方法:一、用强制冷却的方法防止铸件铸态脱碳我厂精铸的35钢、
沥青混凝土结构层被越来越多的应用在高速公路和普通干线公路上,沥青路面的平整度是评定路面质量和使用性能的主要指标之一,公路等级越高,对路面平整度的要求与越高。
Aspha
Ce 不但可控制硫化物夹杂物形态而改进钢的机械性能,而且根据 H.Shimada 等的报告[Corvosion 33,196—9(1977)],Ce 还提供防锈作用。在别处曾报导,在铁锈形成的过程中第一步
在车床上用卡盘夹紧工件进行攻丝,要用与尾座中心对准的丝锥扳手是很麻烦的。为减少麻烦,采用以进给尾座来保持适当的端面压力的办法则是一个巧妙的方法。使用如图所示的攻
在生产中,常遇到图1类型的零件。其圆弧型面加工的传统方法是在平面磨床上先用挤光刀(图2)将砂轮圆周面挤出圆弧为R的凸型面,再以此型面砂轮来磨削零件,达到技术要求。但是,
李春武(中国电视艺术委员会副主任兼秘书长):电视剧《荀慧生》在中央电视台播出以后,产生了很热烈的反响,今天我们在这儿召开一个研讨会,希望各位领导和专家就此展开讨论。
引言首届“宇通杯”已暂告结束,看着渐次离开的身影,心里有些许的不舍、些许的落寞、些许的激情在涌动。大半年的时光,艰辛、执着、关爱、欢笑交织其间,友情之树早已枝叶婆娑