【摘 要】
：
The electrical and optical effects of particles on the nano aluminum film deposited by thermal evaporation was investigated. From the characterization results of scanning electron microscope (SEM), the accumulation in tens of nanometers had been observed.
【机 构】
：
Faculty of Science, Beijing University of Chemical Technology, Beijing 100029, China;China Electroni
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
The electrical and optical effects of particles on the nano aluminum film deposited by thermal evaporation was investigated. From the characterization results of scanning electron microscope (SEM), the accumulation in tens of nanometers had been observed. The current-voltage (Ⅰ-Ⅴ) curve of the sample indicates its nonlinear electrical characters expecting the corresponding nonlinear optical properties. By the theoretical calculation, nonlinear conduction of the carrier transportation may result from the barrier-well-barrier structure, where negative resistance and Coulomb blockade effect appears. The simulation results are approximately matched with the experimental results. By testing the fluorescence emission spectrum of the sample, peaks were found to be located at 420 and 440 nm. In addition, the full width at half maximum (FWHM) had been obviously broadened by means of adding 2, 5-diphenyloxazole (DPO). Therefore, discrete energy levels could be estimated inside those particles.
其他文献
Fugitive dust was cemented, forming larger particles bond in the calcite-consolidation-layer by microbial method. The particular composition, the morphology, and thermal decomposition properties of the samples were characterized by X-ray diffraction (XRD)
Graphene/manganese dioxide composites and grapheme /manganese dioxide/sulfur (G/MnO2/S) composite cathode were prepared by hydrothermal method and by vapor permeation, respectively. Their structure, morphology and specific surface area were characterized
Nanocomposite cation exchange membranes (CEMs) were prepared by adding various loadings of functionalized silica nanoparticles to the sulfonated polyethersulfone (sPES) polymeric matrix. The silica nanoparticles were functionalized by mercaptopropyl (F1,
Expansion joints silicone sealants used in high speed railway construction suffer from ultraviolet radiation(UV),high temperature combined with the alkaline environment.To evaluate the durability and analyse the ageing mechanism,six one-component silicone
A systematic investigation of the graphene oxide composite reduced by either p-phenylenediamine oligomers or hydrazine hydrate was performed with field emission scanning electron microscopy, high resolution transmission electron microscopy, X-ray diffract