The influence of Zr addition on magnetic properties and temperature coefficient for nanocomposite Nd10Fe78.5-xCO5ZrxB6.5 (x=0~4) bonded magnets was investigated. It was found that the room-temperature magnetic properties were remarkably improved with Zr addition due to the grain refinement and increasing volume fraction of the hard magnetic phase. The optimal magnetic properties of Jr=0.689T, iHc=769.4kA·m-1 and (BH)max=84kJ·m-3 were obtained for 2.5% Zr addition. The temperature coefficient of remanence (α) increases slightly and the temperature coefficient of coercivity (β) decreases obviously with increasing Zr content for nanocomposite Nd10Fe78.5-xCo5ZrxB6.5 (x=0~4) bonded magnets.