The morphological evolution of the γ' phase in nickel-based superalloy жc6y during various solution heat treatments was investigated. The significant chan
Zr–Nb–Cr alloys were used to evaluate the effects of alloying elements Nb and Cr on corrosion behavior of zirconium alloys.The microstructures of both Zr subs
The effect of cryogenic temperature on adiabatic shear banding (ASBing) of tungsten heavy alloy (WHA) processed by hot-hydrostatic extrusion was investigated.Re