【摘 要】
：
A new bimetallic complex containing Zn and La was prepared from a salen ligand possessing methoxyl groups at the 3, 3-positions. The structural feature is that
【机 构】
：
Department of Chemistry
论文部分内容阅读
A new bimetallic complex containing Zn and La was prepared from a salen ligand possessing methoxyl groups at the 3, 3-positions. The structural feature is that one of nitrate groups is disordered and displaced between two metal centers. Crystal system: Triclinic space group:P-1, Z=2. a=0.82714(17) nm, b=1.3484(3) (1) nm, and c=1.3898(3) (1) nm, α=79.89(3)°, β=76.67(3)°, and γ=72.43(3)°. V=1.428.6(5) nm3, Dx=1.812 g·cm-3. (Δρ)max=1.510×10-3 enm3, (Δρ)min=-1.503×10-3 enm3. Accordingly, two water molecules occupy the metal centers in the apical positions via the syn-geometry.
其他文献
It has been reported that application of pulsed biases in arc ion plating could effectively eliminate droplet particles.The present paper aims at experimental v
Antimony-doped tin oxide(ATO) nanoparticles were prepared by the mild hydrothermal method at 200 ℃ using sodium stannate, antimony oxide, sodium hydroxide and
The study on arsenopyrite and realgar of bacterial oxidation shows that the chemical behaviors of different arsenic-bearing sulphides oxidated by thermophilic b
The solidified microstructure of immiscible alloys strongly depends on the nucleation, diffusional growth, especially the coalescence of the second phase drople
Copper single crystal specimens with the longitudinal axis parallel to the [013] double-slip-orientation were grown through Bridgman technique. The fatigue test
A nickekdiimine catalyst [N, N-bis(2,6-diisopropylphenyl)-1,4-diaza-2,3-dimethyl-1, 3-butadiene nickel dibromide, DMN] was supported on palygorskite clay for et
Poly (phthalazinone ether sulfone) (PPES) with 1:1 and 1:3 ratios of bisphenol A (BPA) unit to phthalazinone unit were selected as samples. Polymer precipitatio
The density of molten Ni-W alloys was measured with a modified pycnometric method. It is found that the density of the molten Ni- W alloys decreases with temper
Continuous SiC(OAl) fibers, named KD-A fibers, were prepared by the melt-spinning of ceramic precursor polyaluminocarbosilane, air-curing, and pyrolizing at 1 3
A comprehensive experimental and numerical study of solder joints for plastic leaded chip carrier (PLCC) 84-Pin,1.27 mm pitch was carried out. The reliability o