The a alloy Ti-2Al-2.5Zr and near a alloy Ti-4Al-2V were hydrogenated to various levels. The morphology, orientation relation (OR), and habit plane of the hydrides were studied by means of transmission electron microscopy (TEM). It was found that in the two alloys most of the precipitates are δ-hydrides which have fcc structure with the lattice parameter α= 0.44 nm. Two basic orientation relationships and habit planes of the precipitates are determined. Twin structure was observed in both alloys.
The morphology, orientation relation (OR), and habit plane of the hydrides were studied by means of transmission electron microscopy (TEM) . It was found that in the two alloys most of the precipitates are δ-hydrides which have fcc structure with the lattice parameter α = 0.44 nm. Two basic orientation relationships and habit planes of the precipitates are determined. .