CrN/(Ti,Al,Zr,Cr) N bilayer films were successfully deposited on cemented carbide( WC-8% Co) substrates by multi-arc ion plating process using two Ti-Al-Zr alloy targets and one pure Cr target. As a result of bilayered structure and addition of alloying elements( e. g. Al and Cr),the films exhibited excellent high temperature oxidation resistance under both short-term isothermal( up to 800 ℃) and long-term cyclic( up to 600 ℃) exposure conditions. Combined with pre-established outstanding tribological properties( e. g. maximum hardness of 4 000HV0. 01 and maximum adhesion strength over 200 N),these observations make such films quite a promising candidate to extend the cutting tool life span and boost the performance in high-productivity,high-speed and high-feed cutting or in dry machining conditions.
CrN / (Ti, Al, Zr, Cr) N bilayer films were successfully deposited on cemented carbide (WC-8% Co) substrates by multi-arc ion plating process using two Ti-Al-Zr alloy targets and one pure Cr target. As a result of bilayered structure and addition of alloying elements (eg Al and Cr), the films show excellent high temperature oxidation resistance under both short-term isothermal (up to 800 ° C) and long-term cyclic (up to 600 ° C) exposure combined with pre-established outstanding tribological properties (eg maximum hardness of 4000HV0. 01 and maximum adhesion strength over 200 N), these observations make such films quite a promising candidate to extend the cutting tool life span and boost the performance in high -productivity, high-speed and high-feed cutting or in dry machining conditions.