Liquid nitriding of C110 steel was conducted in a wide range of temperatures(400–670 ℃) using a kind of chemical heat-treatments, and the hardness, mechanical
Nanocrystalline/amorphous LaMg11Ni+xNi (x=100%, 200%, mass fraction) composite hydrogen storage alloys were synthesized by ball milling technology. The effects