研究了β钛合金在不同热处理状态下的组织、压缩弹性模量和抗压强度。结果表明,熔炼后的β钛合金组织成分不均匀、晶粒粗大。通过再结晶退火和固溶时效处理后,β钛合金组织稳
论文部分内容阅读
研究了β钛合金在不同热处理状态下的组织、压缩弹性模量和抗压强度。结果表明,熔炼后的β钛合金组织成分不均匀、晶粒粗大。通过再结晶退火和固溶时效处理后,β钛合金组织稳定均匀,抗压强度得到提高,并且其弹性模量值与人体密质骨的弹性模量值接近。
The microstructure, compressive elastic modulus and compressive strength of β-titanium alloy under different heat treatment conditions were studied. The results show that the microstructure of the β Titanium alloy after smelting is not uniform and the grains are coarse. After recrystallization annealing and solution treatment, the microstructure of β-titanium alloy is stable and its compressive strength is improved, and the elastic modulus of β-titanium alloy is close to that of human bone.
其他文献
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
Digital I&C design verification platform includes three parts,which are digital monitoring and control system design verification platform,digital protection sy
在高放废物处置库中,放射性核素由于地下水的侵入而随地下水一同迁移,在多孔介质中由于放射性核素在渗流中的速度不同,必然会产生弥散现象。作为高毒性核素,~(99)Tc在花岗岩
9月28日上午,2017青岛市“威克多·仁洲”杯小学生羽毛球联赛第7轮、第8轮在青岛开发区乒羽俱乐部开赛。比赛开始前,第十三届全运会女子双打冠军骆赢/骆羽前往比赛场地观赛,
核数据重点实验室对散裂靶用核数据之铅、铋、钨和镓的数据进行了评估,同时开展了镓的数据测量。对目前国际上现有微观评价库中的铅、铋、钨、镓的中高能中子反应数据、质子
冷却系统是冷坩埚玻璃固化实验装置中重要的组成部分之一,在运行过程中,多个子系统的关键部件会生成大量的余热,如不及时进行冷却,对实验装置的运行稳定性将产生影响,严重时
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
在当前“调结构,促改革,转变增长方式”的政策下,装备工业亟待整体提升能级。这其中自然包括有效解决防锈难题方面。受全球经济持续低迷的影响,国内装备工业近年来也呈现出起
In order to find out the cause of surface microcrack on 304 austenitic stainless cold rolled coils which is produced in a steel plant of China, lots of studies
~3He正比计数管对中子具有很高的探测效率和较宽的能量响应范围;同时,~3He正比计数管中的介质气体~3He是惰性气体,探测器有着很好的稳定性,适合在较高温度环境下使用。基于以