The waterborne polyurethane/doped Ti O2 nanoparticle hybrid films were prepared. Nd, I doped Ti O2 was prepared with a 50 nm particle size firstly. The hybrid film was prepared by mixing doped Ti O2 with waterborne polyurethane, followed by heat treatment. The presence and nanometric distribution of doped Ti O2 nanoparticles in prepared membranes is evident according to SEM images. The photocatalytic activities of doped Ti O2 were signifi cantly enhanced compared with pure Ti O2 powders. After the hybrid fi lm fabrication, the photocatalytic activities were almost the same as the pure catalysts with kMB of 0.046. In the antibacterial testing, the hybrid fi lms can inhibit E. coli growth. A signifi cant decrease in membrane fl uidity and increase of permeability of E. coli were observed.
The waterborne polyurethane / doped Ti O2 nanoparticle hybrid films were prepared. Nd, I doped Ti O2 was prepared with a 50 nm particle size first. The presence of the hybrid film was prepared by mixing doped Ti O2 with waterborne polyurethane. and nanometric distribution of doped Ti O2 nanoparticles in prepared membranes is evident according to SEM images. The photocatalytic activities of doped Ti O2 were signifi cantly enhanced compared with pure Ti O2 powders. After the hybrid fi lm fabrication, the photocatalytic activities were almost the same as the pure catalysts with kMB of 0.046. In the antibacterial testing, the hybrid fi lms can inhibit E. coli growth. A signifi cant decrease in membrane fl uidity and increase of permeability of E. coli were observed.