J.H.ZHV等研究了经冷、热等静压加工的Ti—6Al-4V合金和以10%TiC粒子增强的Ti—6Al—4V复合材料在538℃的拉伸、蠕变性能. 将Ti—6Al—4V粉末和10%TiC。混合均匀,经冷等静压→真空烧结→热等静压→炉冷,在温度和压力作用下,得
J. H. ZHV et al. Studied the tensile and creep properties of Ti-6Al-4V and Ti-6Al-4V composites reinforced with 10% TiC particles at 538 ℃. Ti-6Al-4V powder and 10% TiC. Mixed, cold isostatic pressing → vacuum sintering → hot isostatic pressing → furnace cooling, under the action of temperature and pressure,