3 mm thick 7050-T7451 aluminum alloy joint was obtained by friction stir welding, and the two-step aging treatment was performed at 121 ℃ × 5 h + 163 ℃× 27 h after welding. Microstructure, hardness profiles and stress corrosion sensitivity of th