【摘 要】
：
研究了防焦剂N-三氯甲基硫代-N-苯基-苯磺酰胺(简称:防焦剂E)用量对三元乙丙橡胶(EPDM)硫化胶的硫化特性、焦烧性能、填料网络及力学性能的影响。结果表明,随着防焦剂E用量的
【机 构】
：
青岛科技大学橡塑材料与工程教育部重点实验室,
论文部分内容阅读
研究了防焦剂N-三氯甲基硫代-N-苯基-苯磺酰胺(简称:防焦剂E)用量对三元乙丙橡胶(EPDM)硫化胶的硫化特性、焦烧性能、填料网络及力学性能的影响。结果表明,随着防焦剂E用量的增大,EPDM硫化胶交联密度和定伸应力均增大,拉断伸长率和压缩永久变形均减小;焦烧时间延长,填料网络化程度增大,拉伸强度和撕裂强度略有下降,无喷霜现象发生。当防焦剂E用量为0.5份时,EPDM硫化胶综合性能较好。
The effects of the amount of anti-coke agent N-trichloromethylthio-N-phenyl-benzenesulfonamide (anti-coke agent E) on the vulcanization, scorch, Filler network and mechanical properties. The results show that with the increase of the amount of anti-scorch agent E, the crosslink density and the ultimate tensile stress of EPDM vulcanizate increase, the elongation at break and the compression set decrease; the scorch time prolongs, the degree of filler network Increased, tensile strength and tear strength decreased slightly, no blooming phenomenon. When the amount of anti-scorch agent E 0.5 parts, EPDM vulcanizate better overall performance.
其他文献
目的：探讨电针对慢性应激抑郁模型大鼠行为学与海马组织环磷酸腺苷(cAMP)含量的影响。方法：40只Sprague-Dawley(SD)大鼠，随机分组为空白组、空白电针组、模型组、电针组、百优解
目的：探讨康复期男性海洛因依赖者(MPHD)神经心理学测验成绩与视觉诱发电位P300(VEP-P300)的关系。方法：采用韦氏记忆量表(WMS)、威斯康星卡片分类测验-改良版(M-WCST)，对38例康
语言类学科的学习要从小处着手,从细微之处着眼,让学生自主学习,在学习中找到乐趣。在当今的英语教学中,教师总会遇到一些学习英语有短板的学生,听力、阅读、写作等每一个阶
研究新近发生的海湾、巴尔干和阿富汗局部战争 ,可以看出由于高科技发展 ,推动武器性能及致伤因素巨大变化[1] 。战争形态已由常规的、全面的战争向大量使用高科技武器装备的
目的：了解和筛查儿童的活动能力、社交能力、学校情况及行为问题的现状。方法：采用Achenbach儿童行为量表，对6～11岁儿童进行调查。结果：儿童社会能力低下及行为问题的检出率分别为
目的：研究爆炸冲击波对大鼠行为学的影响，为阐明冲击伤的作用机制提供实验依据。方法：SD大鼠96只，随机分为对照组、距爆心6、8和10m共四组，在爆后30 h，48h和96h三个时间点，采用大鼠
目前较多的研究显示儿科护士存在抑郁失眠、失眠、注意力不集中、焦虑、情绪不稳定、头痛、胃肠不适等心理和躯体方面的异常。本文对相关文献进行了综述，期望能为全面地了解儿
采用机械共混方法，在乙烯丙烯酸酯橡胶中加入甲基乙烯基硅橡胶共混，研究了纳米白炭黑和纳米炭黑品种及两者并用对MVQ/AEM共混胶的硫化特性、物理机械性能、耐热老化性能、
目的：研究中学生焦虑、抑郁情绪以及与生活事件及应对方式的关系。方法：应用SAS、SDS、青少年生活事件量表，应对方式问卷对210名高三学生进行问卷调查。结果：高三学生焦虑情绪发
研究了白炭黑用量和Si69原位改性对NR/SiO2复合体系结合胶含量及其与动态力学性能之间关系的影响。结果表明,随着白炭黑用量的增大,2种复合体系(NR/SiO2/Si69和NR/SiO2)结合