Based on the harmonic vibration equation, the relationship between IR characteristic peak of fiberglass and Si-O-Si bond angle was deduced, and 1100cm~ -1 characteristic peak was specifically studied. It is found that 1100cm~ -1 characteristic peak shifts to higher wave number when Si-O-Si bond angle increases. Taking fused biconical taper (FBT) coupler as an example, the microstructures of the fiber coupler manufactured at different drawing speeds were tested with micro infrared spectrum. According to the test results, it is found that the bond angle at the taper region is the largest, the one at the fused region is the second largest, and the one of bare fiber is the smallest. The characteristic peaks of fused-taper region shift to higher wave number when drawing speed increases.
Based on the harmonic vibration equation, the relationship between IR characteristic peak of fiberglass and Si-O-Si bond angle was deduced, and 1100cm ~ -1 characteristic peak was specifically studied. It is found that 1100cm Taking fused biconical taper (FBT) couple as an example, the microstructures of the fiber coupler manufactured at different drawing speeds were tested with micro infrared spectrum. According to the test results, it is found that the bond angle at the taper region is the largest, the one at the fused region is the second largest, and the one of bare fibers is the smallest. The characteristic peaks of the fused-taper region shift to higher wave number when drawing speed increases.