为进一步研究UNS N08825合金材料在高腐蚀性气田的耐蚀性能适应性,本文在模拟环境试验条件下,对UNS N08825合金材料进行了应力腐蚀开裂试验及冲刷腐蚀试验研究。试验结果表明,试验用UNS N08825合金材料在该模拟环境试验条件下均具有较好的耐应力腐蚀开裂性能和耐冲刷腐蚀性能。
In order to further study the corrosion resistance adaptability of UNS N08825 alloy material in the highly corrosive gas field, the UNS N08825 alloy material was subjected to stress corrosion cracking test and erosion corrosion test under simulated environmental test conditions. The test results show that the UNS N08825 alloy has good stress corrosion cracking resistance and erosion resistance under the simulated environmental test conditions.