A kind of ceramic slurry was prepared and sprayed onto the surface of 9Ni steel at room temperature. The coating layer will not only reduce the depth of the formed Ni-enriched entanglement at high temperature but also have an excellent ability to resist o
【机 构】
：
State Key Laboratory of Multi-phase Complex Systems, Institute of Process Engineering, Chinese Acade
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
A kind of ceramic slurry was prepared and sprayed onto the surface of 9Ni steel at room temperature. The coating layer will not only reduce the depth of the formed Ni-enriched entanglement at high temperature but also have an excellent ability to resist oxidation of the 9Ni steel. Compared to bare specimen, the depths of the entanglement of the coated 9Ni specimen could be successfully reduced by 74.1%and the oxidation loss be decreased by 62.3% by heating at 1 250 ℃ for 60min. In addition, the coated specimen indicates no trace of oxide pegs. It proves that the coating has outstanding improvement to internal oxidation resistance. Some characterization methods such as metalloscopy, XRD, XPS, SEM and EDX have been used to reveal a possible protective mechanism. The result shows that the coating layer reacts with the iron oxide to form MgFe2O4 on the surface of the coated specimen, which could provide a smaller diffusion coefficient rate of Fe ion. The coating with a low cost and easy implementation is promisingly applicable in the slab-reheating process of the 9Ni steel.
其他文献
Bio-ceramsite technology is one of the most effective technologies in the pretreatment of drinking water. In this work, bio-ceramsite was fabricated byCitrobacter freundii (C. freundii) immobilization on the ceramsite. Thefi ndings of the current study su
In order to investigate the carbide dissolution mechanism of high carbon-chromium bearing steel during the intercritical austenitization, the database of TCFE7 of Thermo-calc and MOBFE of DICTRA software were used to calculate the elements diffusion kinet
The high grade non-oriented electrical steel sheets containing 3.0%Si were manufacturing processed using different cutting techniques, then they were stress relief annealed(SRA), the profiles and textures of the cutting edges were compared before and afte
Ion transport of sandwich cementitious materials (SCM) exposed to chloride environment was investigated by accelerated diffusion method and natural diffusion method. Pore structure and micromorphology of SCM were investigated by MIP and SEM-EDS. In compar
Ni-plated glass beads (GB) was obtained by electroless plating, based on PVC adhesive, Ni-plated GB/PVC composite was prepared. Temperature insulation, fire retardation and microwave absorption properties were tested, the results showed that the nickel co