Monodisperse crosslinked poly(chloromethylstyrene-co-divinylbenzene)(poly(CMSt-co-DVB))microsphereswere prepared by distillation-precipitation copolymerization of chloromethylstyrene(CMSt)and divinylbenzene(DVB)inneat acetonitrile.The polymer particles had clean surfaces due to the absence of any added stabilizer.The size of the particlesranges from 2.59 μm to 3.19 μm and with mono-dispersity around 1.002-1.014.The effects of monomer feed incopolymerization on the microsphere formation were described.The polymer microspheres were characterized by SEM andchlorinity elemental analysis.
Monodisperse crosslinked poly (chloromethylstyrene-co-divinylbenzene) (poly (CMSt-co-DVB) microsphereswere prepared by distillation-precipitation copolymerization of chloromethylstyrene (CMSt) and divinylbenzene (DVB) inneat acetonitrile.The polymer particles had clean surfaces due to absence of any added stabilizer. The size of the particlesranges from 2.59 μm to 3.19 μm and with mono-dispersity around 1.002-1.014. These effects of monomer feed incopolymerization on the microsphere formation were described described polymer microspheres were characterized by SEM andchlorinity elemental analysis.