The modification mechanism of Nd on Al-25Si alloy was studied. The result showed that pure Nd (0.3%) could significantly refine primary silicon in hypereutectic
Nanocrystalline monoclinic and cubic Gd2O3:Eu with different Eu^3+ concentration were prepared using glycinenitrate combustion synthesis. By changing the ratio