【摘 要】
：
To obtain the influence laws of the fine gangue rate on the properties of coal gangue cementitious paste, the slump, divergence, stratification, bleeding, setting time and mechanical strength with the change of fine gangue rate were studied on the basis o
【机 构】
：
School of Civil and Safety Engineering, Dalian Jiaotong University, Dalian 116028, China;The State K
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
To obtain the influence laws of the fine gangue rate on the properties of coal gangue cementitious paste, the slump, divergence, stratification, bleeding, setting time and mechanical strength with the change of fine gangue rate were studied on the basis of keeping the amount of cementing material and slurry concentration unchanged. The porosity and the distribution of pore diameter of the filling specimen for curing 28 d were tested by a mercury injection instrument under different fine gangue rate conditions. It was shown that the slump, divergence, setting time and compressive strength of the paste firstly increased and then decreased with increasing fine gangue rate. The stratification and bleeding rate decreased with increasing fine gangue rate. The smaller the critical pore size of the paste was, the smaller the porosity was, the smaller the average pore size was. When the fine gangue rate was 40％, the maximum critical pore diameter of the paste was 55.79 μm, and the corresponding porosity was 17.54％, and the properties of filling paste were the best. When the fine gangue rate further increased, the aggregate surface area increased, and the reaction product of cementitious materials could not effectively fill the pores. It weakened the agglomeration effect. The particles surface of coal gangue was fragmental and flake deposit with irregular shape and uneven fold morphology. It was easy to be bonded with the surface of other filling material. The hydration products of coal gangue cementitious material were a large number of C-S-H gel with fibrous shape and ettringite (AFt) with compact block structure. The theoretical reference was provided for the preparation of low cost gangue cemented filling materials in coal mines.
其他文献
Plasma-enhanced CVD (PECVD) epitaxy at 200 oC was used to deposit heavy doped n-type silicon films. Post-annealing by rapid thermal processing was applied to improve the properties of the epitaxial layer. By analyzing the Raman spectra and the imaginary p
In order to investigate how to enhance the teeth fracture resistance after the post and core treatment, an in vitro study was conducted to measure the fracture resistance of endodontically treated teeth restored with cast post and core with two kinds of s
The effect of spherical particle size on the surface morphology, electrochemical property and processability of lithium iron phosphate was systematically studied. Spherical lithium iron phosphate with different particle size distributions controlled with
A modified co-precipitation method for the production of Cu/ZnO/Al2O3 complex was studied. The modification was that part of Al was introduced by adding Al3+ into Cu2+/Zn2+ solution, and the rest of Al was added after co-precipitation step in the form of
A new method of fabricating C/C composite materials, namely electric heating CVD method, was used, which electrified the carbon fiber directly by using the conductivity of itself. Acetylene was used as the carbon source with nitrogen as dilution gas, and
Zn2SnO4/few-layer boron nitride nanosheets (FBNNS) hybrids were synthesized via a one-step hydrothermal method. The structures, morphology, optical properties, electron transformation and separation of the as-prepared products were characterized by X-ray
The rare earth doped TiO2 was prepared and characterized with Nd,Ho and Y as the doping agents,which have obvious absorption in visible light area.The particle size of the glomeration was about 200-400 nm.TiO2 sensor performed a significant change in resi
Red mud was firstly used as a raw material in sintering field road cement. Then, the radioactive element distribution characteristics of red mud based field road cement (RFC) before and after hydration were comparatively investigated. The experimental res
Phase pure ZrB2-SiC composite powders were prepared after 1 450 ℃/3 h via carbothermal reduction route,by using ZrSiO4,B2O3 and carbon as the raw materials.The influences of firing temperature as well as the type and amount of additive on the phase compos
The Lap-joint configuration and the vacuum assisted forming method were put forward to meet the demands of the compression bending strength and the strong connection between the steel and FRC.The bending mechanic tests of the Lap-joint bending specimens c