High-g Impact Resistance for Epoxy Molding Compound
【机 构】
:
National Key Laboratory of Science and Technology on Electronic Test and Measurement,North Universit
【出 处】
:
武汉理工大学学报(材料科学版)(英文版)
【发表日期】
:
2010年4期
其他文献
An Analytical Method to Detect the Coupling Damage Relationship of Concrete Subjected to Bending Fat
Structure and Properties of Ti-Si-N Coatings Synthesized by Combining Cathode Arc and Middle-frequen
Ti-Si-N composite coatings were synthesized on a novel combining cathode and middle-frequency magnetron sputtering system,designed on an industrial scale.Ti was produced from the arc target and Si from magnetron target during deposition.The influences of
The behavior that different magnetic treatment directions induce various amounts of welding residual stress reductions in low alloy steel was studied.Reductions of 26%-28% in the lon-gitudinal stress σ_x were obtained when low frequency alternating magnet
Relationship between leucite content and compressive strength of K2O-Al2O3-SiO2 sys-tem dental glass ceramics were investigated. 10 groups of feedstock powder with different composi-tions were treated according to the same thermal treatment system of leuc
The elastic microstrains in a crystallite of electrodeposited nanocrystalline copper were investigated by analyzing the high resolution electron microscopy(HRTEM)image.The mi-crostrain was considered as consisting of two parts,in which the uniform part wa
Nano SiO_2/NR composites were prepared through blending nano SiO_2 emulsion with natural rubber latex and then concreting with acetic acid.The emulsion nano SiO_2 was prepared with Na_2SiO_3·9H_2O and hydrochloric acid under the reaction of the assistant