A systemic investigation was done on the chemistry and crystal structure of boundary phases in sintered Ce9Nd21FebalB1(wt%) magnets. Ce2Fe14B is believed to be more soluble in the rare-earth(RE)-rich liquid phase during the sintering process. Thus, the grain size and oxygen content were controlled via low-temperature sintering, resulting in high coercivity and maximum energy products. In addition, Ce formed massive agglomerations at the triple-point junctions, as confirmed by elemental mapping results. Transmission electron microscopy(TEM) images indicated the presence of(Ce,Nd)Ox phases at grain boundaries. By controlling the composition and optimizing the preparation process, we successfully obtained Ce9Nd21FebalB1 sintered magnets; the prepared magnets exhibited a residual induction, coercivity, and energy product of 1.353 T, 759 k A/m, and 342 k J/m3, respectively.
A systemic investigation was done on the chemistry and crystal structure of the boundary phases in the sintered Ce9Nd21FebalB1 (wt%) magnets. Ce2Fe14B is believed to be more soluble in the rare earth (RE) -rich liquid phase during the sintering process. Grain size and oxygen content were controlled via low-temperature sintering, resulting in high coercivity and maximum energy products. In addition, Ce formed massive agglomerations at the triple-point junctions, as confirmed by elemental mapping results. Transmission electron microscopy (TEM) images indicated the presence of (Ce, Nd) Ox phases at grain boundaries. By controlling the composition and optimizing the preparation process, we successfully obtained Ce9Nd21FebalB1 sintered magnets; the prepared magnets showed a residual induction, coercivity, and energy product of 1.353 T, 759 k A / m, and 342 k J / m3, respectively.