The glass-forming ability (FGA) of Nd70-xFe20Al10Yx and Nd60-xFe30Al10Yx(0≤x≤15) alloys produced by Cu mold casting was investigated.Except Y=5 at.pct,bulk am
The Mg65Cu25Y10 melts were quenched at a temperature of 973 K under various pressures in the range of 2~5 GPa and ambient pressure. The microstructure of the sol