Tensile tests of GH4169 alloy were performed at room temperature. Different fractions, distributions and shapes of δ phase was prepared by aging treated at 880 °C, 930 °C and 980 °C for 5 h or 10 h. The effect of δ phase on the mechanical properties of GH4169 alloy was investigated. The results show that 0.2% yield strength and ultimate tensile strength of GH4169 alloy increase by 61 MPa and 78 MPa respectively when the fraction of δ phase increases from 2.20% to 5.21%. Then, the ultimate tensile strength remains at 1 012 MPa even when the fraction of δ phase reaches 7.56%. The fraction effect of δ phase on the strength improvement of GH4169 alloy is more significant than morphology, and the critical fraction value is 5.21%. In addition, the elongation decreases by 14.1% when the fraction of δ phase increases from 2.20% to 7.56%. Excessive needle or short rod shaped δ phase is responsible for the reduction of elongation.
Tensile tests of GH4169 alloy were performed at room temperature. Different fractions, distributions and shapes of δ phase was prepared by aging treated at 880 ° C, 930 ° C and 980 ° C for 5 h or 10 h. The effect of δ phase on the mechanical properties of GH4169 alloy were investigated. The results show that 0.2% yield strength and ultimate tensile strength of GH4169 alloy increase by 61 MPa and 78 MPa respectively when the fraction of δ phase increases from 2.20% to 5.21%. Then, the ultimate tensile strength remains at 1 012 MPa even when the fraction of δ phase reaches 7.56%. The fraction effect of δ phase on the strength improvement of GH4169 alloy is more significant than morphology, and the critical fraction value is 5.21%. When the fraction of δ phase increases from 2.20% to 7.56%. Excessive needle or short rod shaped δ phase is responsible for the reduction of elongation.