The powder crystals of RMnO 3 (R=Er, Tm) with hexagonal and orthorhombic structures were prepared under hydrothermal conditions. The different structural phases of the title compounds were controllably formed from different kinds of precursors at different reaction temperatures. All of the samples were characterized by powder X-ray diffraction, scanning electron microscopy, inductively coupled plasma analysis, and variable temperature magnetic susceptibility. Their structures were refined by Rietveld method from powder X-ray diffraction data. The measurement of magnetic behavior shows antiferromagnetic orderings at Neel temperatures around 80 and 40 K for the hexagonal and orthorhombic phases, respectively.
The different structural phases of the title compounds were controllably formed from different kinds of precursors at different reaction temperatures. All of the samples were characterized by powder X-ray diffraction, scanning electron microscopy, inductively coupled plasma analysis, and variable temperature magnetic susceptibility. Their structures were refined by Rietveld method from powder X-ray diffraction data. The measurement of magnetic behavior shows antiferromagnetic orderings at Neel temperatures around 80 and 40 K for the hexagonal and orthorhombic phases, respectively.