对某厂未作焊后热处理的液化石油气储罐进行H_2S腐蚀挂片检测表明,腐蚀产物主要为FeS.经过分析认为,只要严格控制H_2S含量,即使焊缝存在轻度的焊接残余应力(<.6σ_Y),在两三年的运行期内并不一定发生应力腐蚀问题。
H_2S corrosion coupons tests on a liquefied petroleum gas tank which has not been post-welded heat-treated by a factory show that the corrosion products are mainly FeS. The analysis shows that, as long as the H 2 S content is strictly controlled, the problem of stress corrosion does not necessarily occur during the two or three year operation even though the weld has slight welding residual stress (<.6σ_Y).