采用固相合成法制备了Li1-xCrxFePO4/C(x=0,0.01,0.02,0.03,0.04),实验结果表明:采用固相合成法制备的Cr掺杂LiFePO4/C具有完善的LiFePO4橄榄石型晶体结构。发现在Cr的掺入量为0.02摩尔分数时,表现出较好的循环性能和充放电性能,在0.1C倍率充放电时,放电比容量为159.8mAh/g。