TiO2 fibers were prepared via alternatively introducing water vapor and Ti precursor carried by N2 to an APCVD(chemical vapor deposition under atmospheric pressure) reactor at ≤200 °C. Activated carbon fibers(ACFs) were used as templates for deposition and later removed by calcinations. The obtained catalysts were characterized by scanning electron microscopy(SEM) ,transmission electron microscopy(TEM) ,Brunauer,Emmett and Teller(BET) and X-ray diffraction(XRD) analysis. The pores within TiO2 fibers included micro-range and meso-range,e.g.,7 nm,and the specific surface areas for TiO2 fibers were 141 m2/g and 148 m2/g for samples deposited at 100 °C and 200 °C(using ACF1700 as template) ,respectively. The deposition temperature significantly influenced TiO2 morphology. The special advantages of this technique for preparing porous nano-material include no consumption of organic solvent in the process and easy control of deposition conditions and speeds.
TiO2 fibers were prepared via alternatively introducing water vapor and Ti precursor carried by N2 to an APCVD (chemical vapor deposition under atmospheric pressure) reactor at <200 ° C. Activated carbon fibers (ACFs) were used as templates for deposition and later removed by calcinations . The obtained catalysts were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), Brunauer, Emmett and Teller (BET) and X-ray diffraction -range, eg, 7 nm, and the specific surface areas for TiO2 fibers were 141 m2 / g and 148 m2 / g for samples deposited at 100 ° C and 200 ° C using ACF1700 as template, respectively. influenced TiO2 morphology. The special advantages of this technique for preparing porous nano-material include no consumption of organic solvent in the process and easy control of deposition conditions and speeds.