The compressive strength and flexural strength with the same strength class cement mortar of the alkali-resistant glass fiber cement mortar were tested in standard and hot-water curing condition, and the damage mechanism of alkali-resistant glass fiber was studied. The interaction mechanisms of the chemical erosion and physical injury in different curing conditions were studied in order to summarize the damage mechanism of alkali-resistant glass fiber in cement-based materials, and chloride diffusivity coefficient and porosity of cement mortar were tested in the different curing conditions. The experimental results are that the strength of cement based materials and fiber cement slurry interface zone were closely related, and heat curing could accelerate the hydration of cement, but inevitably enlarge the defect.
The compressive strength and flexural strength with the same strength class cement mortar of the alkali-resistant glass fiber cement mortar were tested in standard and hot-water curing condition, and the damage mechanism of alkali-resistant glass fiber was studied. The interaction mechanisms of the chemical erosion and physical injury in different curing conditions were studied in order to summarize the damage mechanism of alkali-resistant glass fiber in cement-based materials, and chloride diffusivity coefficient and porosity of cement mortar were tested in the different curing conditions. results are that the strength of cement based materials and fiber cement slurry interface zones were closely related, and heat curing could accelerate the hydration of cement, but inevitably enlarge the defect.