Applying negative bias voltages caused significant microstructure changes in arc ion plated CrN films. Nanocrystalline microstructures were obtained by adjustin
A systematic investigation of the microstructure of CrAICχN1-χ coatings as a function of carbon contents was conducted.Quaternary CrAICχN1-χ coatings were d