BaZr1-xScxO3-0.5x (x=0.07,0.10,0.13,0.16) powders were prepared by solid-state reaction method,and ZnO was used as sintering aid.Samples with different amount of ZnO additive were sintered at 1450 ℃ for 6 h in air.Single cubic perovskite phase proton cond