【摘 要】
：
采用有限元软件ProCAST模拟TiAl基合金液在金属型真空吸铸成形铸造工艺中的充型凝固过程,分析在充型凝固过程中产生缺陷的原因,并进行了相关的实验验证。在模拟过程中发现铸
论文部分内容阅读
采用有限元软件ProCAST模拟TiAl基合金液在金属型真空吸铸成形铸造工艺中的充型凝固过程,分析在充型凝固过程中产生缺陷的原因,并进行了相关的实验验证。在模拟过程中发现铸件中确实存在模拟预测的缺陷,且缺陷主要集中在叶片隼部,在叶身部位出现少量的缩松缺陷,模拟和实际相吻合。
The finite element software ProCAST was used to simulate the filling and solidification process of TiAl-based alloy liquid in the process of metal-based vacuum casting and casting. The causes of defects during filling and solidification were analyzed and the relevant experimental verification was carried out. In the process of simulation, it is found that there is indeed a defect in the prediction of the casting, and the defects are mainly concentrated in the falcons of the blade. A small amount of shrinkage defects appear in the blade parts. The simulation and the actual are in good agreement.
其他文献
目的:研究失同步化缺血性心力衰竭心肌内向整流钾电流(IK1)的变化及其心脏再同步化治疗(CRT)的作用.方法:取西北犬行左束支射频消融术和冠状动脉前降支结扎术建立失同步化缺
通过开展生姜高产栽培技术示范，采用优选良种、科学栽培、加强田间管理、及时防治病虫害、按市场需求适时挖收的一系列技术管理措施，取得了较好的示范作用。
采用拉伸速率突变法,研究Ti-29Nb-13Ta-5Zr(Ti-29-13)合金冷轧后在700～800℃和5×10-4～1×10-2s-1应变速率范围内的高温变形行为和变形机制,并与典型β钛合金Ti-15V-3Cr-3Sn-3A
在变频、变温和不同应变振幅下,对不同热处理后的新型阻尼TNCH-Z钛合金的低频阻尼特性进行研究,同时对该合金的声频内耗进行测量。结果表明:室温低频范围内,合金的阻尼性能受
以氯化钠作为造孔剂,利用金属注射成形(MIM)工艺制备多孔钛。研究烧结温度、造孔剂粒度和含量对多孔钛孔隙度、微观形貌和力学性能的影响。结果表明,随着烧结温度的升高,多孔
杂草的识别分类在精准农业的变量喷施中具有重要的作用.因此提出了一种新的基于SVM(支持向量机),利用决策二叉树在可见/近红外图像中识别作物和杂草的方法.根据近红外波段的
采用中频感应熔炼制备Nd0.75Mg0.25(Ni0.8Co0.2)3.5储氢合金,在0.03 MPa氢气氛围进行退火,退火温度分别为850,900和950℃,保温时间均为7h.分别对合金的电化学性能、气态储氢
对新型第3代粉末高温合金母合金、等离子体旋转电极法生产(PREP)粉末和热等静压态合金中的微量元素Hf,Zr和Ta的存在相进行了研究。结果表明:母合金中微量元素Hf,Zr和Ta主要以
采用浆料包渗法,以TiO2粉为渗Ti源,纯Al粉为还原剂,NH4Cl作为活化剂,Al2O3为惰性添加剂,蛋白质(鸡蛋清)为粘结剂,在Cu表面预先镀Ni随后表面浆料包渗Ti-Al,制备Ti-Al共渗层。
通过X-Y向拉伸强度、Z向剥离强力、NOL环整体拉伸强度表征预制体性能,研究了炭布叠层针刺预制体的结构特点.结果表明:X-Y向拉伸强度反映了针刺对连续纤维的损伤程度,其随针刺