【摘 要】
：
运用高温合成的方法合成SrBPO5:Eu2+,Mn2+,用X射线衍射仪(XRD)、红外光谱仪(IR),以及荧光光度计(PL)对合成产物的结构和发光性质进行了研究。XRD测试结果表明,在1000℃下烧结
【机 构】
：
应用电化学新技术重点建设实验室,桂林理工大学材料科学与工程学院,广西建筑新能源与节能重点实验室,广西大学化学化工学院,
论文部分内容阅读
运用高温合成的方法合成SrBPO5:Eu2+,Mn2+,用X射线衍射仪(XRD)、红外光谱仪(IR),以及荧光光度计(PL)对合成产物的结构和发光性质进行了研究。XRD测试结果表明,在1000℃下烧结6h得到SrBPO5单相。发光光谱测试表明,在350nm紫外线激发下,宽带发射最强峰位于400nm和498nm处,当Mn2+含量进一步增加时,发射光颜色从蓝色向蓝白色移动,测试结果说明SrBPO5:Eu2+,Mn2+有希望应用于白色LED方向。
SrBPO5: Eu2 + and Mn2 + were synthesized by high temperature synthesis. The structures and luminescent properties of the synthesized products were investigated by XRD, IR and PL. XRD results show that sintering at 1000 ℃ for 6h gives SrBPO5 single phase. Luminescence spectra showed that the strongest peak of broadband emission was located at 400nm and 498nm under the excitation of UV at 350nm. When the content of Mn2 + was further increased, the emission color shifted from blue to blue-white. The results show that SrBPO5: Eu2 + and Mn2 + are promising Applied to white LED direction.
其他文献
在硅浓度一定的前提下,分别采用莫来石纤维复合及六亚甲基二异氰酸酯单体(HDI)修饰两种方式对氧化硅气凝胶进行力学性能增强,并对其进行结构与力学性能的表征.结果表明,在力
利用磁控溅射方法在泡沫镍(Ni)基底上成功制备出大面积多层石墨烯薄膜,利用拉曼光谱仪、X射线衍射仪、扫描电子显微镜(SEM)和电化学工作站等对其结构和性能进行了表征。结果
分别采用十六烷基三甲基溴化铵(CTAB)以及偶联剂γ-氨丙基三乙氧基硅烷(KH550)对锂皂石进行修饰,制备有机化的锂皂石(Laponite)。然后将有机化的锂皂石与聚丙烯(PP)进行熔融
以酶解木质素(EHL)和胱氨酸为原料,通过Mannich反应制备了胱氨酸改性酶解木质素(EHL-g-Cys)。研究了反应温度、反应时间对EHL-g-Cys的产率和接枝率的影响。红外光谱和元素分
以木质素磺酸钠(LS-Na)、丙烯酰胺(AM)、马来酸酐(MAH)为原料,膨润土(Bentonite)为无机添加剂,过硫酸钾(KPS)为引发剂,N,N-亚甲基双丙烯酰胺(NMBA)为交联剂,采用溶液接枝共聚
采用溶液共混法制备了一系列不同比例的魔芋葡甘聚糖(KGM)/羟丙基纤维素(HPC)共混膜,研究了KGM含量对共混膜的力学性能、透光性、吸湿性能等的影响。结果表明,当KGM含量为10%
将化学还原法制备的Ni-Zr-B非晶态合金催化剂用于硝基苯液相加氢制苯胺的反应,并通过XRD,TEM和H2-TPD技术对催化剂进行表征,研究了Zr含量对Ni-Zr-B催化剂微观结构和其催化加
利用自反应淬熄法制备了一种Ba-Zn铁氧体空心陶瓷微珠材料,在此基础上,通过超声波化学镀,在其表面进行镀Ni-Co合金层.通过SEM、EDS和XRD分析,结果表明,该材料具有中空结构,主
用乙酰丙酮还原氧化石墨制备得到石墨烯,其可在水、丙酮、N,N-二甲基甲酰胺等极性溶剂中超声分散,其中以水作为溶剂其分散性最好(浓度约为0.7g/L)。通过原子力显微镜(AFM)测
以多孔材料SiO2气凝胶微球为基体,吸附熔融态石蜡制备成石蜡/SiO2复合相变材料并制成复合相变涂料;将SiO2气凝胶微球制成隔热涂料,将复合相变涂料和隔热涂料交替涂覆制成涂料