Vortical structures of a submarine with appendages are fully turbulent and complex.Thus,flow control and vortex manipulation are of great importance for the hydrodynamic performance and acoustic characteristics.Take the generic submarine model DARPA Suboff as the test case,a vortex tuning method based on the Liutex force field is proposed to manipulate the vorticity field.Viscous flow past the submarine model in straight-line motion at a Reynolds number of 1.2×107 is achieved by solving the Reynolds averaged Navier-Stokes(RANS)equations.Multi-block structured mesh topology is used to discretize the computational domain,and the shear stress transport(SST)k-ω turbulence model is implemented to close the equations.The control of vortex is achieved by introducing additional source terms based on Liutex vortex definition and identification system to the RANS equations.The resistance acting on the submarine,flow field as well as the vortical structures are compared and analyzed.Results show that Liutex force model can effectively reduce the resistance by 9.31%and change the vortical structures apparently.
其他文献
研究了用电解精炼法从粗铟中去除杂质金属锡铅,考察了阴极板厚度、槽电压、电流密度、电解液pH和电解温度对阴极铟中锡铅含量的影响。结果表明:在阴极板厚度2 mm、槽电压80 mV、电流密度90 A/m2、电解液pH为2.0~2.2、电解温度24~28℃条件下,粗铟一次电解后,阴极铟中锡铅质量分数均小于2×10-4%,达到行业标准YS/T 257—2009中In99.995要求。
研究了采用氧压碱浸—水浸工艺从高砷铅阳极泥中两段脱砷,考察了浸出时间、温度、液固体积质量比等对砷脱除率的影响。结果表明:在液固体积质量比4/1、氢氧化钠质量浓度110 g/L、温度120℃、浸出时间4 h、氧气压力0.8 MPa、搅拌速度500 r/min条件下进行碱浸,在液固体积质量比3/1、温度75℃、浸出时间1 h、搅拌速度500 r/min条件水浸,最终砷脱除率在94%以上,脱砷效果较好。
研究了用P204从硫酸体系中萃取分离铟、镓,考察了水相硫酸初始浓度、搅拌速度、萃取时间、有机相P204体积分数、相比等因素对铟、镓萃取的影响。结果表明:在水相初始硫酸质量浓度100 g/L、搅拌速度250 r/min、萃取时间5 min、相比Vo/Va=1/3条件下,用20%P204+260#溶剂油作萃取剂,经三级逆流萃取,铟萃取率为99.8%,镓萃取率小于1%,铟、镓得到有效分离。
The significance of riparian vegetation on river flow and material transport is not in dispute.Conveyance laws,sediment erosion and deposition,and element cycling must all be adjusted from their canonical rough-wall boundary layer to accommodate the prese
研究了在铝棒表面通过挤压复合技术包覆铅银合金得到Al基铅合金复合阳极,并在硫酸锌溶液中以500 A/m2恒电流条件下极化48 h,采用X射线衍射、扫描电子显微镜、循环伏安法、阳极极化和交流阻抗法等分析阳极表面氧化膜层物相、形貌及电化学性能,采用显微图像分析仪和数显显微硬度计表征合金金相及硬度,并通过电子拉伸试验测定阳极的极限抗拉强度.结果表明:所制备的Al基复合阳极为Al基Pb-0.2%Ag和Al基Pb-0.75%Ag;合金中银含量增加,合金阳极的析出氧过电位降低,催化活性及耐腐蚀性能提高,合金组织的晶型
PDC复合片固体废料中含有少量钴。研究了采用酸浸—草酸盐沉淀法回收钴。以硫酸为浸出剂,草酸铵为沉淀剂,考察了硫酸浓度、浸出时间、搅拌速度、浸出温度对钴浸出率的影响。结果表明:钴浸出率随硫酸浓度、搅拌速度提高及浸出时间延长而提高;在硫酸浓度0.2 mol/L、温度20℃、搅拌速度400 r/min条件下浸出6 h,钴浸出率在90%以上,浸出效果较好。
研究了采用氯化铵-盐酸体系从烧结电除尘灰中浸出金属铅,考察了氯化铵浓度、盐酸浓度、固液质量体积比、浸出温度、浸出时间对铅浸出率的影响,并探讨了浸出机制。结果表明:在NH4Cl浓度2 mol/L和HCl浓度1.5 mol/L、浸出温度70℃、浸出时间30 min、固液质量体积比为1 g/4 mL条件下,铅浸出率为98.6%;NH4Cl的加入可以提高溶液氢离子活度,实现低酸浓度下铅的有效浸出。
When studying the flow dynamics and the characteristics of fluid motion,vortex structure with their interactions is the key issue.In the present work,a vortex control method is investigated based on the vortex identification system of Liutex.The numerical
根据热力学数据,绘制了25℃条件下NdCl3-AlCl3-NH4HCO3体系在总碳浓度为1.0 mol/L条件下各组分的lg cB-pH曲线,以及在不同总碳浓度条件下Al与Nd的lg cB-pH曲线;分析了用碳酸氢铵沉淀稀土时各组分的行为。结果表明:pH在2.8~7.0范围内,可实现Nd2(CO3)3沉淀;pH在2.8~3.7范围内,铝不易与稀土共沉淀,