Fe(NO3)3水溶液经加热回流制得α-Fe2O3纳米粒子,在焙烧温度为800℃时可与NaOH反应生成NaFeO2固体碱催化剂。用TEM、TGA、XRD等方法对前驱物或催化剂进行了表征。试验结果显
论文部分内容阅读
Fe(NO3)3水溶液经加热回流制得α-Fe2O3纳米粒子,在焙烧温度为800℃时可与NaOH反应生成NaFeO2固体碱催化剂。用TEM、TGA、XRD等方法对前驱物或催化剂进行了表征。试验结果显示:当催化剂用量为3%,醇油摩尔比为12∶1,催化大豆油酯交换反应5h,大豆油的转化率高达94.88%。该催化剂具有较高的稳定性,催化剂重复使用时其催化活性基本不变。
Fe (NO3) 3 aqueous solution was heated to reflux α-Fe2O3 nanoparticles, the calcination temperature is 800 ℃ reaction with NaOH NaFeO2 solid base catalyst. The precursors or catalysts were characterized by TEM, TGA and XRD. The results showed that the conversion of soybean oil reached 94.88% when the amount of catalyst was 3%, the molar ratio of alcohol to oil was 12:1, and the transesterification of soybean oil was catalyzed 5h. The catalyst has high stability, and the catalytic activity of the catalyst is not changed substantially when used repeatedly.
其他文献
对国内外粘纤生产设备现状进行了分析研究并对我国粘胶短纤生产设备国产化问题从三个方面论述了自己的观点。
The status quo of viscose fiber production equipment at ho
联合利华饮食策划作为全球领先的专业餐饮解决方案提供者,始终关注、发现和研究餐饮行业的趋势和食客对于餐饮的需求,凭借其在国际餐饮市场的网络地位和本土实践的成功经验,
为迎接经济全球化的挑战,我国粘胶纤维生产必须加强技术改造,形成经济规模,降低成本,提高质量,创造更好的经济效益。在九十年代以前,我国的粘胶短纤维生产线单线生产能力小,
高脂蛋白血症是动脉硬化发病的首要因素。糖尿病人动脉硬化发病率远较非糖尿病人高,约1/3的糖尿病人有高脂蛋白血症。糖尿病人血浆极低密度脂蛋白(VLDL),低密度脂蛋白胆固醇
心血管系统疾病的免疫学问题所涉及的方面很多,本文拟就以下几个主要问题作一简述。风湿热和风湿性心脏病急性风湿热的发生与A组乙型溶血性链球菌(以下简称乙链菌)感染有关,
随着世界经济的重心向亚洲转移,以及由于持续的经济高增长和人口增加,从现在起到2010年,亚洲的能源需求必将翻番。中东、新的中亚各共和国和俄罗斯的远东地区储藏有大量的石
在对学生进行纪律和道德品质教育过程中,常常发现学生有说和做不一致的现象.比如说,课堂常规和学生守则,他们能说得头头是道,背得滚瓜烂熟,可是实际上有的要求却做不到;有时
<正>在中学历史教学中复习课十分重要.通过复习能够巩固学过的知识,使学过的知识系统化,有助于理解新的知识.复习课的类型一般分为课堂复习、单元复习和总复习.单元复习也称
观察8名吸烟者(其中男女各半),平均年龄25岁,吸烟时能量消耗明显增加,由2,230升至2,445 kcal/24h,但基础代谢率则无影响。此外,在吸烟期间,即每24小时抽24支烟,尿排泌去甲肾
本文报告了216例SLE,男15例,女201例,年龄8～65岁。主要临床表现包括发热、关节痛、皮疹及肝脾肿大、肾炎等,光敏感及脱发也较常见。作者分析了SLE的实验室异常,发现本组患者LE