【摘 要】
：
对进口结构钢Ａ５３７和国产结构钢Ｅ３６模拟节点热点处应力状态制成接头试件，采用极大似然性原理组织试验，考察材料、介质（空气和海水）、工艺（焊后或焊修）对接头疲劳强度的影响，并获得这两种钢的
论文部分内容阅读
对进口结构钢Ａ５３７和国产结构钢Ｅ３６模拟节点热点处应力状态制成接头试件，采用极大似然性原理组织试验，考察材料、介质（空气和海水）、工艺（焊后或焊修）对接头疲劳强度的影响，并获得这两种钢的焊接接头的概率－应力范围－寿命曲线（Ｐ－Ｓ－Ｎ），对比管节点疲劳试验结果，表明“焊接接头疲劳寿命相对于管节点疲劳试验的启裂寿命”观点是安全的。
The joint specimens were made on the hot spot of the imported structural steel A537 and the domestic structural steel E36, and the microstructure was tested by the method of maximum likelihood. The material, medium (air and seawater), technology (after welding or welding repair) On the fatigue strength of the joints, and the probability-stress range-life curve (P-S-N) of the welded joints of the two kinds of steels was obtained. The fatigue test results of the joints of the welded joints showed that the fatigue life of welded joints was Test Kai life expectancy "point of view is safe.
其他文献
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
通过拉伸、冲击试验研究了预应变量和时效温度对厚壁X80HD2大变形直缝埋弧焊管低温冲击韧性的影响,测定了不同应变时效条件下的夏比冲击吸收能量和剪切断面率,用扫描电镜观察
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
对屈服强度700 MPa级超高强度热轧钢带进行了700~800℃退火处理,通过光学显微镜、扫描电镜、透射电镜及性能测试对不同温度退火后试验钢的组织性能进行分析。结果表明,700~80
在濑户内海家岛海域未被破坏的自然生态系,使之形成中型围隔生态系。在6m以上浅海水域人为形成富营养化,由于古卡盾氏藻(Chattonella antiqua)导致赤潮发生,海洋生态系受到破
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
本文通过计算和对比分析，得到１９９１年春、夏江淮地区特大暴雨形成的五个基本特征：西北太平洋上副高显著偏西、偏北；较弱的西南季风与东南气流汇合成强西南气流伸向江淮地区；偏东风与强
全球海平面上升将会带来的严重影响,已引起世界各国政府和科学家的广泛关注。一九九一年,联合国环境规划署发布的“当前全球环境状况”中指出:“全球变暖将会加速海平面升高
海岸风Ｅ．Ｐ．Ｖｅｓｅｌｏｖ（原苏联水文气象中心）表面风对河口风暴潮有相当大的影响。向岸狂风经常引起岸边水位暴涨，给工业造成巨大损失。另一方面，离岸风使岸边水位下降，阻碍了吃水线深的轮船的正常