【摘 要】
：
通过建立微球燃料元件模型,对U10Mo-Al弥散型燃料在不同辐照条件下的辐照肿胀性能进行模拟计算,结果表明:辐照温度越高,燃料肿胀越明显;随着裂变率的增加,在燃耗拐点以前,燃
【机 构】
：
四川大学教育部辐射物理及技术重点实验室,中国工程物理研究院,中国核动力研究设计院,
论文部分内容阅读
通过建立微球燃料元件模型,对U10Mo-Al弥散型燃料在不同辐照条件下的辐照肿胀性能进行模拟计算,结果表明:辐照温度越高,燃料肿胀越明显;随着裂变率的增加,在燃耗拐点以前,燃料的肿胀速率基本相同,在燃耗拐点以后,裂变率大的燃料肿胀较慢;与实验数据点进行比较,在合理的范围内理论值和实验值相一致。
The model of the microsphere fuel element was established to simulate the irradiation and swelling behavior of the U10Mo-Al dispersed fuel under different irradiation conditions. The results show that the higher the irradiation temperature, the more obvious the fuel swelling. With the increase of the fission rate The fuel swellowing rates are basically the same before the fuel burn point, and the fuel with large fission rate swelled slowly after the burnup inflection point. Compared with the experimental data, the theoretical and experimental values are within a reasonable range.
其他文献
AIM:To examine the growth inhibitory effects of Phyllanthus emblica (P.emblica) and Terminalia belierica (T.bellerica) extracts on human hepatocellular carcinom
参照锆合金中的第二相成分,熔炼2种不同Fe/Cr比的Zr(Fe,Cr)2(Fe/Cr=2和0.5)和ZrCr2(Fe/Cr=0)3种试验合金,对它们进行压力-成分-温度(P-C-T)测试和吸放氢动力学测试。同时用XR
基于微观相场理论,利用Khachaturyan所给原子间作用势与长程序参数关系方程得出L12结构第一近邻原子间作用势推演公式,反演出Ni-Al-Fe合金L12结构第一近邻原子间作用势。反演
研究TC11钛合金片层组织在两相区980-850℃,0.001,0.01和0.1 s
由于CdZnTe(CZT)探测器尺寸和能量分辨率受到工艺限制,采用电容性Frisch栅探测器结构,将多个薄的单元探测器并行叠加使其等效为大体积的探测器,用于克服单元小探测器探测效率
采用分子动力学模拟研究了单壁碳纳米管的力学特性与其长度、直径及手性的关系.在施加拉伸或压缩载荷时,不同直径的单壁碳纳米管表现出明确的力学性能变化.锯齿型和扶手椅型
利用气态源分子束外延在InP衬底上生长了具有InxGa1-xAs或InxAl1-xAs连续递变缓冲层的高In组分In0.78Ga0.22As探测器结构.通过原子力显微镜、X射线衍射、透射电子显微镜和光
对GH4199合金进行不同时间的高密度电脉冲处理,研究高密度电脉冲下合金组织的演化及处理后的拉伸性能.结果表明,高密度电脉冲显著加速合金中原子的扩散,与常规时效状态相比,
利用热化学气相沉积法在负载不同厚度催化剂的硅纳米丝(SiNW)表面生长碳纳米管(CNTs),探讨了生长条件对所合成SiNW-CNT的结构和场发射特性的影响.这种类似树状的三维结构具有
利用SEM、XRD和EDS研究Y对Ti45Al8Nb(at%)合金在900℃空气中的循环氧化行为的影响。实验结果表明,适量Y的加入显著提高了合金的抗循环氧化性。无Y合金300次循环后便出现了表