The isothermal oxidation behavior of a new Refree nickel-based single-crystal superalloy in air at 950 ℃ for 200 h was studied by scanning electron microscopy(SEM)with energy-dispersive spectroscopy(EDS)and X-ray diffraction(XRD).The results indicate that oxidation kinetics obeys parabolic law approximately,and the mass gain increases rapidly during initial oxidation stage and then gradually slows down.The oxidation scales are composed of three layers:the outer layer mainly consists of NiO with a small amount of CoO;the intermediate layer is mainly composed of Cr_2O_3 with a small amount of spinel compounds such as CrTaO_4,NiCr_2O_4,CoCrAl_2O_4,CoAl_2O_4,and NiAl_2O_4;and the inner layer is composed of Al_2O_3.Inner Al_2O_3 layer suppresses the diffusion of elements between oxygen and alloy elements,slows down the alloy oxidation speed,and also suppresses the growth of the oxide scale and reduces the oxidation rate,which is agreeable with the oxidation kinetics. The isothermal oxidation behavior of a new Refree nickel-based single-crystal superalloy in air at 950 ° C for 200 h was studied by scanning electron microscopy (SEM) with energy-dispersive spectroscopy (EDS) and X-ray diffraction (XRD) results indicate that oxidation kinetics obeys parabolic law approximately, and the mass gain increases rapid during initial oxidation stage and then gradually slows down. oxidation scales are composed of three layers: the outer layer mainly consists of niO with a small amount of CoO; the The intermediate layer is composed mainly of Cr 2 O 3 with a small amount of spinel compounds such as CrTaO 4, NiCr 2 O 4, CoCrAl 2 O 4, CoAl 2 O 4, and NiAl 2 O 4; and the inner layer is composed of Al 2 O 3 .Inner Al 2 O 3 layers suppresses the diffusion of elements between oxygen and alloy elements, slows down the alloy oxidation speed, and also suppresses the growth of the oxide scale and reduces the oxidation rate, which is agreeable with the oxidation kinetics.