【摘 要】
：
针对新型耐候钢06CuPNi1Cr2镍铬较高的特点,从转炉热态模拟和真空精炼对其进行研发试验研究。转炉模拟试验顶吹氧气强度为3.0~3.3m3/(min.t),底吹氮气强度为0.02~0.05m3/(min
【机 构】
：
北京科技大学冶金与生态工程学院生态与循环冶金教育部重点实验室,中国镍资源控股有限公司,
论文部分内容阅读
针对新型耐候钢06CuPNi1Cr2镍铬较高的特点,从转炉热态模拟和真空精炼对其进行研发试验研究。转炉模拟试验顶吹氧气强度为3.0~3.3m3/(min.t),底吹氮气强度为0.02~0.05m3/(min.t),终点碳质量分数小于0.05%,温度大于1 610℃。精炼试验真空度为0.06MPa,出钢温度为1 620~1 650℃,钢水成分达到06CuPNi1Cr2钢的成分设计要求。
Aiming at the high characteristic of new type of weathering steel 06CuPNi1Cr2 Ni-Cr, the R & D test was carried out from the converter thermal simulation and vacuum refining. The top-blowing oxygen intensity was 3.0-3.3m3 / (min.t) in converter simulation test. The bottom-blowing nitrogen intensity was 0.02-0.05m3 / (min.t). The end-point carbon mass fraction was less than 0.05% and the temperature was more than 1 610 ℃. The vacuum degree of refining test is 0.06MPa, tapping temperature is 1 620 ~ 1 650 ℃, and the composition of molten steel reaches 06CuPNi1Cr2 steel composition design requirements.
其他文献
大力促进生产,促进购销,扩大財源,这是毛主席的理財思想,我们任何时候都必须坚决贯彻,一点也不能动搖。到底財政部门怎样促进生产,同志们发表了不少意见,有的很好。我认为,
老年肺结核特征及防治重点黄辉近几十年来，由于有效抗痨药物的广泛使用和防痨工作的开展，使全人群的肺结核患病率、死亡率显著下降，由此老年肺结核的患病率、死亡率则显示上升趋
据《华商报》载．网名“草野”的日籍华人在日本某地设立VoIP服务器．招揽客户低价拨打国际电话．但全部国际长途话费却要由宝鸡电信支付．从2006年1月1日至2月8日短短 40天总共要支
2006年中国邮政改革、发展和稳定的任务依然十分艰巨。但无论是改革还是稳定,都不能偏离发展这条主线,从这个意义上说,对于邮政改革与稳定,发展既是目的,也是手段。笔者认为,
最近在美国华盛顿召开的第97届美国胃肠道病协会的年会（消化道疾病周）上报道了BritishBiotech公司的血小板激活因子拮抗剂来昔帕泛（lexipafant，商品名Zacutex）能降低急性胰腺炎患
文章阐述了黑河下游正义峡至狼心山河段水量平衡研究的目标、内容及预期成果。
This article elaborates the goals, contents and expected results of the research on wa
形同而病异，治病需求本──１例右肺中部结核空洞误诊为肺脓疡男，２７岁，工人。因发热、咳吐大量脓痰，外周血白细胞（ＷＢＣ）增高，右肺中部厚壁空洞而于当地卫生院以肺脓疡治疗，经大剂量联合应用多
过去,在湖北宜都市红花套镇部分山区,因为穷,小伙子找对象是“踏破铁鞋无觅处”。如今或依靠科技发家致富,或外出打工出息,外地姑娘便格外青睐红花套镇的小伙子了。红花套镇
校园网工程是一项技术性较强的综合工程,它涉及到网络交换设备、路由设备、服务器与工作站、校园网应用软件、传输介质等许多方面。选择一个理想的、适合学校特点的校园网方
“从前有座山,山上有个庙,庙里有个和尚……”年轻的陶兆龙听5岁的女儿又在唱这首古老的歌谣,不禁哑然失笑,伸出大手掌在女儿结实的小屁股上拍了一下,“唱错了,重唱!”“从